Introduction
| Test items | PA-3016（Adhesive） | PA-9001（Hardener） |
|---|---|---|
| Solid content（%） | 50±2 | 100% |
| Solvent | Ethyl acetate | None |
| 25℃，mpa.s（Viscosity） | 50-200 | 1750-3250 |
| Mixing ratio | 100 | 3.6 |
| Test items | PA-3018（Adhesive） | PA-9001（Hardener） |
|---|---|---|
| Solid content（%） | 50±2 | 100% |
| Solvent | Ethyl acetate | None |
| 25℃ mpa.s（Viscosity） | 50-200 | 1750-3250 |
| Mixing ratio | 100 | 4 |
Features and advantages
- Excellent performance when bonding with the second generation PVDF membrane material.
- Fast curing speed.
- High initial strength after curing.
- Resistant to high temperature and humidity for a long time.
- The fastness of EVA composite adhesive layer does not decrease after thermal encapsulation.
- Excellent coating performance.
- Good leveling performance.
- Superior UV aging resistance.
- No wrinkle defects after compound curing.
Application process
Coating method
Suitable for mainstream coating methods such as mesh rolls, blades, extrusion, etc.
Drying temperature
Suggested temperature: 80-100℃, according to drying situation.
Coating dry weight
8-10 g/m² is recommended.
Maturation conditions
For 50-60℃, suggested maturation time is 2-3 days. Can be adjusted and customized according to customer process.